Raw data collection for the publication  P. Pötschke, T. Villmow, B. Krause and B. Kretzschmar, Influence of Twin-screw Extrusion Conditions on MWCNT Length and Dispersion and Resulting Electrical and Mechanical Properties of Polycarbonate Composites

<p>This data collection contains the raw data for the publication&nbsp;<br>Petra P&ouml;tschke, Tobias Villmow, Beate Krause and Bernd Kretzschmar, Influence of Twin-screw Extrusion Conditions on MWCNT Length and Dispersion and Resulting Electrical and Mechanical Properties of Polycarbonate Composites, <strong>polymers </strong>2024, 16(19), 2694. <a href="https://doi.org/10.3390/polym16192694">https://doi.org/10.3390/polym16192694</a></p> <p>The data are sorted according to the figures and tables in which they are used.</p> <p>The description in Table 1 is taken from the reference:<br>Villmow, T.; Kretzschmar, B.; P&ouml;tschke, P. Influence of screw configuration, residence time,&nbsp;<br>and specific mechanical energy in twin-screw extrusion of polycaprolactone/multi-walled carbon nanotube composites. Compos. Sci. Technol. 2010, 70, 2045-2055. doi: https://doi.org/10.1016/j.compscitech.2010.07.021.</p> <p>Figure 15 is adapted from the references:<br>Krause, B.; Boldt, R.; P&ouml;tschke, P. A method for determination of length distributions of multiwalled carbon nanotubes before and after melt processing. Carbon 2011, 49, 1243-1247, https://doi:10.1016/j.carbon.2010.11.042.<br>and<br>Liebscher, M.; Domurath, J.; Krause, B.; Saphiannikova, M.; Heinrich, G.; P&ouml;tschke, P. Electrical and melt rheological characterization of PC and co-continuous PC/SAN blends filled with CNTs: Relationship between melt-mixing parameters, filler dispersion, and filler aspect ratio. Journal of Polymer Science Part B: Polymer Physics 2018, 56, 79-88, https://doi:10.1002/polb.24515.<br>The data are reused with permissions.&nbsp;</p> <p>The raw data (TEM images) used for the calculation of the carbon nanotube length distributions and mean carbon nanotube length values shown in Figs. 4, 11, 13, 16, and 17 are publically available at:&nbsp;Krause, B. (2024). Transmission electron microscopy (TEM) images of multiwalled carbon nanotubes (MWCNT) detached from polycarbonate (PC) composites [Data set]. Zenodo. https://doi.org/10.5281/zenodo.11400466</p> <p>Version v2:</p> <p>Compared to the submitted figure, in the final version in<strong> Fig. 9 </strong>the sample using the side feeder (PC-H-05) was removed and two samples extruded at 15 kg/h and 750 rpm (PC-H-25) and 1000 rpm (PC-H-26) were added. In the text-file the unit of GPa for the elastic modulus was corrected to MPa.&nbsp;</p> <p>Compared to the submitted Table, in the final version of <strong>Table 2 </strong>the electrical resistivity values were given in more detail including the standard deviation. The column title of sigma break was changed to sigma max, which is more correct for these stress-strain diagrams.</p> <p>Compared to the submitted Table, in the final version of <strong>Table 3</strong> the column title of sigma break was changed to sigma max, which is more correct for these stress-strain diagrams.The title of the first column was set to "screw" instead of "feeding". &nbsp;</p>